Sharpness testing of micro-objects such as miniature diamond tool tips

Description

CROSS-REFERENCES TO RELATED APPLICATION

This application is a continuation-in-part of U.S. patent application Ser. No. 09/774,400, filed Jan. 30, 2001 now abandoned, the entire disclosure of which is incorporated by reference for all purposes.

BACKGROUND OF THE INVENTION

The present invention relates generally to the manufacture and testing of micro-objects such as shaped tool heads or tips, and more particularly to the manufacture and testing of miniature tools incorporating or consisting of shaped structures.

Manufacturing and other processes pertaining to scanning probe microscopy, nanomachining, micromachining, machining, optics, biotechnology, and biomedicine often require highly specialized miniature tools. Such tools typically consist of a shaped tool head formed and parted from a diamond or other hard material workpiece and mounted on a body or handle. Present methods do not satisfactorily enable determining the sharpness or fineness of the tool head prior to its mounting to the tool body.

BRIEF SUMMARY OF THE INVENTION

According to an aspect of the invention, a micro-object having a desired sharp point or edge may be optically tested during fabrication. This is accomplished by applying a known force to the workpiece against an optically opaque layer disposed on a transparent substrate, passing light down the workpiece toward the opaque layer, and determining whether the shaped portion of the workpiece has sufficiently penetrated the opaque layer so that light passed through the workpiece can be detected on the remote side of the transparent substrate. If the light is not detected, the shaped portion of the workpiece is considered to be insufficiently sharp, and the workpiece can be subjected to further shaping operations. While it is possible to perform this testing during the process of aligning and embedding the micro-object in the reference structure, it is generally preferred to perform this testing when the workpiece is being shaped.

In an alternative arrangement, after the force is applied to cause penetration of the opaque layer by the shaped portion of the workpiece, the substrate and the workpiece are moved laterally with respect to one another so as to form a scratch on the opaque layer. The workpiece can be removed from the vicinity of the opaque layer and the amount of light transmitted through the scratch can be measured. If the amount of light is sufficient, the shaped portion of the workpiece is considered to be sufficiently sharp.

A further understanding of the nature and advantages of the present invention may be realized by reference to the remaining portions of the specification and the drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a partial side view of a workpiece that may be tested using embodiments of the present invention;

FIG. 1B is a partial side view of a tool tip bonded to a cantilever;

FIG. 2 is a side plan view of an arrangement for sharpness testing of a workpiece according to principles of the present invention; and

FIG. 3 is a side plan view of an alternative arrangement for sharpness testing of a workpiece according to principles of the present invention.

DESCRIPTION OF SPECIFIC EMBODIMENTS

FIG. 1A is a schematic side plan view of a workpiece used in fabricating and testing micro-objects. The micro-objects may subsequently be mounted on supporting structures. In the illustrated embodiment, the ultimate micro-object is formed from a shaped portion 10 of a workpiece 15 having a central axis 17. The particular techniques for shaping the end of the workpiece 15, parting the shaped portion of the workpiece from the remainder of the workpiece, and mounting the resultant micro-object on a supporting structure are not a part of the invention, and will not be described in detail. Suffice it to say that the shaped portion may be formed by techniques such as chemically or abrasively lapping, etching, laser forming, ion milling or nano-machining.

FIG. 1B shows the parted micro-object, designated 20, mounted to a supporting structure 25. In this particular application, the micro-object is a tool tip bonded to a cantilever.

It should be noted that the term micro-object refers to objects having dimensions in the tens of microns to hundreds of microns. However, the sharpness (measured in terms of a radius of curvature) of such micro-objects is in the nanometer range. Further, the workpiece from which micro-objects are made according to embodiments of the invention have dimensions in millimeters. For example a typical diamond workpiece might be 10-12 mm long and have a transverse rectangular or triangular cross sectional configurations with dimensions on the order of 4-5 mm.

The material of workpiece 10 depends on the application of the micro-object. If the micro object is to define a tool tip, the workpiece is typically composed of a hard material such as diamond, cubic boron nitride, carbon nitride, titanium nitride, tungsten carbide, titanium carbide, silicon nitride, or other materials. In some applications, such as microlenses, hardness of the workpiece is not the primary criterion, and the material can be chosen to satisfy other requirements such as providing desired optical properties. The shaped portion 10 is preferably of pyramidal, conical, blade or other sharp configuration known in the art. However, for some other applications, such as microlenses, the shaped portion may have a rounded shape (e.g., spherical, aspheric, cylindrical, etc.). However, the present invention is likely to find less usefulness when the shaped portion is rounded.

In a specific application, the micro-object is a diamond tool tip having a pyramidal shape (three sides and a triangular base or four sides and a quadrilateral base), and the supporting structure is a silicon cantilever structure. The axis 17 may be chosen to correspond to one of the diamond's hard axes (100 or 101).

Preferably, the sharpness of shaped portion 10 is tested prior to further steps in the fabrication of the composite tool. Such pre-testing typically involves a penetration or controlled scratch of a surface with a known force, analysis of the penetration or scratch providing a go/no go indication of a particular state of sharpness. Such pre-testing has the advantage of allowing determination of the suitability for intended purpose of shaped portion 10 before workpiece 15 is parted so as to permit rework as necessary.

FIG. 2 illustrates one approach for testing the sharpness of shaped portion 10 according to principles of the present invention. The technique includes forming an optically opaque layer of material 105 on one side of a substrate 110 and providing an optical detector 115 with suitable collection optics on the other side of substrate 110. Substrate 110 is preferably composed of a transparent or semi-transparent material having an index of refraction that matches or is greater than that of workpiece 15. The measurement is effected by exerting a known force 120 against workpiece 15, causing shaped portion 10 to penetrate opaque layer 105, and directing light 125 into workpiece 15 so as to propagate along workpiece 15 toward shaped portion 10. The penetration depth depends on the hardnesses of workpiece 15 and opaque layer 105, force 120, and the sharpness of shaped portion 10. The technique extracts information regarding the sharpness by determining information regarding the depth of penetration. Alternatively, workpiece 15 and/or substrate 110 may be composed of a non-transparent material. In such case, sharpness information may be similarly extracted through the use of electromagnetic radiation, other than light, such as infrared, medium infrared, ultraviolet and soft x-ray.

Initial design requires a determination of the thickness of opaque layer 105 and the force 120 to be applied. This is done by assuming that shaped portion 10 has a sharpness corresponding to the minimum sharpness that will be considered acceptable for incorporation into a composite structure. It is then straightforward to determine a thickness of the opaque material and a force such that force 120 causes shaped portion 10, having such an acceptable degree of sharpness, to penetrate opaque layer 105 to a depth that is within the tunneling distance of transparent substrate 110. The computation provides a series of possible thickness-force value pairs that can be used. The choice can be made by restricting the thickness and force to practical values. For example, force 120 should be small enough so as not to subject workpiece 15 to possible damage, while the thickness should be large enough to provide the needed opacity. In some instances, it may be desirable to have a composite layer structure on transparent substrate 110. This composite layer structure may include a thin layer of soft highly opaque material underlying a harder layer of material having less opacity. A possible configuration for such a layer structure includes a composite comprising a 2-micron aluminum layer, a 500-nm tungsten layer, a 100-nm titanium layer, and a quartz layer. Thus, if force 120 is sufficient to cause shaped portion 10 to penetrate the harder material, the softer opaque material will be penetrated easily.

There are a number of possible test protocols. For example, the test can be run so if an insufficiently sharp shaped portion 10 provides transmitted light 125 below a threshold, workpiece 15 is withdrawn from the vicinity of opaque layer 105 and the end of workpiece 15 subjected to further shaping operations. Alternatively, it is possible, in the event that the transmitted light 125 is below the threshold, to increase force 120 to an additional known value, and if the transmitted light 125 is now above the threshold, to flag shaped portion 10 as being suitable for parting and mounting for use in a less demanding application.

FIG. 3 shows an alternative configuration in which substrate 110 and workpiece 15 are moved laterally with respect to one another (by relative rotation or translation) after shaped portion 10 has penetrated opaque layer 105. This causes shaped portion 10 to scratch opaque layer 105. Workpiece 15 is then removed from the vicinity of opaque layer 105 and the amount of light 125 transmitted through the scratch is measured. If the amount of light 125 is sufficient, shaped portion 10 is considered to be sufficiently sharp. This technique has the additional advantage of testing for mechanical defects in shaped portion 10. If shaped portion 10 fractures when subjected to the transverse forces caused by the relative movement workpiece 15 can be reworked before shaped portion 10 is parted from the workpiece.

Although the invention has been described in terms of illustrative embodiments, the above description should not be taken as limiting the scope of the invention as defined by the claims.