Method for determining hydrogen mobility as a function of temperature in superconducting niobium cavities

Description

The United States of America may have certain rights to this invention under Management and Operating contract No. DE-AC05-84ER 40150 from the Department of Energy.

FIELD OF THE INVENTION

The present invention relates to a method for determining the mobility of hydrogen as a function of temperature in niobium cavities and more particularly to such a method that utilizes a relatively simple and straight forward ion chamber radiation detector based system for such determination.

BACKGROUND OF THE INVENTION

Niobium and hydrogen can form a niobium hydride surface coating on superconducting niobium cavities at approximately 100° K. The niobium hydride interrupts the superconducting properties of the cavity surface and causes what is commonly referred to as “Q disease”. A superconducting niobium cavity suffering from Q disease must be put through a costly time and energy thermal cycle to remove the effects of Q disease. Determining the mobility of hydrogen as a function of temperature in superconducting niobium cavities can contribute significantly to the understanding of conditions that promote or cause Q disease. It would therefore be highly useful to have a method for determining the mobility of hydrogen as a function of temperature in superconducting niobium cavities.

OBJECT OF THE INVENTION

It is therefore an object of the present invention to provide have a method for determining the mobility of hydrogen as a function of temperature in superconducting niobium cavities.

SUMMARY OF THE INVENTION

According to the present invention, there is provided a method for determining the mobility of hydrogen as a function of temperature in superconducting niobium cavities comprising: 1) heating a cavity under test to remove free hydrogen; 2) introducing hydrogen-3 gas into the cavity; 3) cooling the cavity to allow absorption of hydrogen-3; and 4) measuring the amount of hydrogen-3 by: a) cooling the cavity to about 4° K while in the presence of a regulated amount of tritium gas in the cavity; b) allowing the cavity to warm at a stable rate to 4.22° K; c) allowing the cavity to warm to room temperature and as it warms flowing high quality helium gas through the cavity; and d) directing the exit gas to an ion chamber radiation detector.

DESCRIPTION OF THE DRAWINGS

FIG. 1 is a process flow diagram for the hydrogen mobility determination process of the present invention.

DETAILED DESCRIPTION

As depicted in FIG. 1, the method of the present invention comprises: 1) heating a cavity under test in a vacuum to remove free hydrogen; 2) introducing hydrogen-3 gas into the cavity; 3) cooling the cavity to allow absorption of hydrogen-3; and 4) measuring the amount of hydrogen-3 by: a) cooling the cavity to about 4° K while flowing a known and regulated amount of helium into the cavity; b) allowing the cavity to warm at a known stable rate from 4.22° K to room temperature; and c) directing gas exiting the chamber to an ion chamber radiation detector that measures current from tritium beta particle energy in the gas exiting the chamber.

After introduction of the hydrogen-3 gas into the hydrogen purged cavity, sufficient time must be allowed to elapse for hydrogen exchange between the hydrogen and hydrogen-3 to fully occur. Such residence can require several hours, but is readily determinable by trial and error for any specified niobium cavity. Allowing the cavity to cool after introduction of the radioactive hydrogen-3 and passage of a suitable residence time allows for tens of milligrams (tens of Curies) of hydrogen-3 to be absorbed by the niobium surface. Such levels of radioactivity are readily detectable by the ion chamber radiation detector as current produced from tritium beta particle energy in the exit gas.

As the helium carrier gas that is circulated through the cavity during warming exits the cavity, it may be necessary to mix the carrier gas with about one part in ten of an organic gas, such as methane, to achieve proper ion chamber function.

The ion chamber radiation detector measures current from tritium beta particle energy deposited in the helium carrier gas. The rate of hydrogen devolution as the cavity warms is proportional to the ionization current in the ion chamber radiation detector. Care must be exercised in the design, construction and operation of the ion chamber radiation detector to insure that a “guard” detector is utilized to correct for background ionizing radiation associated with radioactive contaminants in the construction materials and the effects of cosmic ray interactions on the detector.

The various apparatus used in the successful practice of the present invention are well known in the art as are the manipulative techniques for obtaining the cooling, heating and transfer of the detector and carrier gases described herein and useful ion radiation detectors useful in the successful practice of the invention are commercially available.

There has thus been described a method that can be used to identify the rate at which hydrogen devolves from the surface of a niobium cavity as a function of the temperature of that cavity and hence the term during which treatment to remove hydrogen from the surface of a niobium superconductive cavity must be conducted to inhibit the development of Q disease.

As the invention has been described, it will be apparent to those skilled in the art that the same may be varied in many ways without departing from the spirit and scope of the invention. Any and all such modifications are intended to be included within the scope of the appended claims.