Multifunctional crosslinkers for shape-memory polyimides, polyamides and poly(amide-imides) and methods of making the same

Description

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent application Ser. No. 13/557,326, filed Jul. 25, 2012, which claims the benefit of U.S. Provisional Patent Application No. 61/636,134, filed on Apr. 20, 2012, and U.S. Provisional Patent Application No. 61/636,170, filed Apr. 20, 2012, all of which are incorporated herein by reference in their entirety.

RIGHTS OF THE GOVERNMENT

The invention described herein may be manufactured and used by or for the Government of the United States for all governmental purposes without the payment of any royalty.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates generally to the field of multifunctional crosslinkers. More particularly, it relates to tri- and tetrafunctional amine crosslinkers that may be used to create crosslinked polyimide, polyamide, and poly(amide-imide) polymers and films having shape memory properties at elevated temperatures and methods of making the same.

2. Description of the Related Art

Shape memory materials, including shape memory polymers (SMPs) and shape memory alloys (SMAs) are a class of active materials that can be programmed to “fix” a temporary shape or a series of temporary shapes and to recover to a “memorized” permanent shape upon application of a predetermined external stimulus. The permanent shape of most SMPs is established during the manufacturing process by a network of covalent or physical crosslinking. While the shape memory effects of SMAs stem from martensitic/austenitic transitions (changes in crystal structure), the shape memory effect of thermally-induced SMPs is driven by heating the polymer above its glass transition temperature (T_g) or melting point (T_m), which causes the SMP to become soft and elastomeric in nature. The heated SMP may be deformed into one or more temporary shapes. The SMP is then cooled below the T_g or T_m while still under stress, causing immobilization of the constituent network chains to fix the temporary shape. Recovery of the permanent shape is then accomplished by heating the SMP above the T_g or T_m, which remobilizes the network chains and allows rubber (entropic) elasticity to return the SMP to its equilibrium or permanent shape. Corresponding to the nature of the external stimulus, other types of SMPs include light-induced, electro-active, pH-responsive, and water/moisture-driven SMPs.

SMPs and SMAs have been widely used in actuation, robotics, and piping, as components in aircraft and automobiles, and in medical and dental applications. SMPs possess many properties that make them more attractive than SMAs, such as much lower cost, easier manufacturing and processing using conventional methods, higher capacities for elastic deformation (up to 200% in most cases), lower density, and a broader range of customizable application temperatures. In addition, many SMPs have the potential for biocompatibility and biodegradability. However, most currently available SMPs consist of high-alkyl content polymers such as polyurethane, poly(ε-caprolactone), poly(norbornene), (ethylene-oxide)/(ethylene terephthalate)-based copolymers, styrene/butadiene copolymers, thiolene/acrylate copolymers, etc. Many of these SMPs do not possess shape memory properties above 150° C., nor do they possess long-term thermal and thermo-oxidative stability in this temperature region.

Aromatic polyimides, polyamides, and poly(amide-imides) are common classes of heat-resistant, thermally stable polymers with glass-transition temperatures in the excess of 150° C. The solubility of the polymers in common organic solvents may be improved by introducing wholly aromatic groups containing meta-phenoxyphenol (—OC₆H₄—OC₆H₅) or meta-oxyphenylene-meta-oxyphenoxy (—OC₆H₄O—C₆H₄O—) moieties to the main chains or side chains of the polymer backbones. The addition of crosslinkers introduces a covalent network structure into these polymers, which imparts programmable shape-memory effects.

SUMMARY OF THE INVENTION

The present invention includes a trifunctional crosslinker having the following general structure A, in which W is selected from a group consisting of CH₃C, N, P═O, or BO₃ (which may alternatively be written as B(—O)₃), with R being selected from a group consisting of —F, —Cl, —CF₃, or —CH₃ and the amine groups (NH₂) being located meta or para with respect to R:

The present invention further includes a method for synthesizing the trifunctional crosslinker having general structure A in which W is selected from the group consisting of CH₃C, N, and B(—O)₃, the method comprising the steps of: mixing, in a polar, aprotic solvent, potassium carbonate, a tris(hydroxyphenyl) compound that is selected from the group consisting of 1,1,1-tris(4-hydroxyphenyl)ethane, tris(4-hydroxyphenyl)amine, and tris(4-hydroxyphenyl)borate, and a halogenated nitrobenzene having the following general structure:

in which X is a halogen such as —F or —Cl; R is —H, —F, —Cl, —CF₃, or —CH₃; and the nitro group (—NO₂) is either meta or para with respect to R. A tris(nitrophenoxy)phenyl compound is formed by this mixture. The method concludes with reducing the tris(nitrophenoxy)phenyl compound by catalytic hydrogenation in the presence of 5% palladium on activated carbon in a hydrogen atmosphere to form the trifunctional crosslinker.

In one embodiment of the method, the halogenated nitrobenzene is selected from the group consisting of 1-fluoro-4-nitro-benzene, 1-chloro-4-nitro-benzene, 1,2-difluoro-4-nitro-benzene, 1,2-dichloro-4-nitro-benzene, 1-fluoro-2-methyl-4-nitro-benzene, 1-chloro-2-methyl-4-nitro-benzene, 1-fluoro-2-(trifluoromethyl)-4-nitro-benzene, 1-chloro-2-(trifluoromethyl)-4-nitro-benzene, 1-methyl-2-chloro-4-nitrobenzene, 1-methyl-2-fluoro-4-nitro-benzene, 1-(trifluoromethyl)-2-chloro-4-nitro-benzene, 1-methyl-2-fluoro-4-nitro-benzene.

In another embodiment, W is CH₃C, and the trifunctional crosslinker is selected from the group consisting of 1,1,1-tris[4-(2-fluoro-5-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-fluoro-4-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-chloro-5-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-chloro-4-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-trifluoromethyl-5-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-trifluoromethyl-4-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-methyl-5-aminophenoxy)phenyl]ethane, and 1,1,1-tris[4-(2-methyl-4-aminophenoxy)phenyl]ethane.

In yet another embodiment, W is N, and the trifunctional crosslinker is selected from the group consisting of tris[4-(4-aminophenoxyl)phenyl]amine, tris[4-(2-fluoro-5-aminophenoxy)phenyl]amine, tris[4-(2-fluoro-4-aminophenoxy)phenyl]amine, tris[4-(2-chloro-5-aminophenoxy)phenyl]amine, tris[4-(2-chloro-4-aminophenoxy)phenyl]amine, tris[4-(2-trifluoromethyl-5-aminophenoxy)phenyl]amine, tris[4-(2-trifluoromethyl-4-aminophenoxy)phenyl]amine, tris[4-(2-methyl-5-aminophenoxy)phenyl]amine, and tris[(4-(2-methyl-4-aminophenoxy)phenyl]amine.

In a further embodiment, W is B(—O)₃, and the trifunctional crosslinker is selected from the group consisting of tris[4-(4-aminophenoxyl)phenyl]borate, tris[4-(2-fluoro-5-aminophenoxy)phenyl]borate, tris[4-(2-fluoro-4-aminophenoxy)phenyl]borate, tris[4-(2-chloro-5-aminophenoxy)phenyl]borate, tris[4-(2-chloro-4-aminophenoxy)phenyl]borate, tris[4-(2-trifluoromethyl-5-aminophenoxy)phenyl]borate, tris[4-(2-trifluoromethyl-4-aminophenoxy)phenyl]borate, tris[4-(2-methyl-5-aminophenoxy)phenyl]borate, and tris[4-(2-methyl-4-aminophenoxy)phenyl]borate.

The present invention further includes a method for synthesizing the trifunctional crosslinker having general structure A in which W is P═O, the method comprising the steps of: oxidizing tris(4-methoxyphenyl)phosphine with aqueous hydrogen peroxide to form tris(4-methoxyphenyl)phosphine oxide; demethylating the tris(4-methoxyphenyl)phosphine oxide by heating in pyridine hydrochloride to form tris(4-hydroxyphenyl)phosphine oxide; mixing, in a polar, aprotic solvent, the tris(4-hydroxyphenyl)phosphine oxide, potassium carbonate, and a halogenated nitrobenzene having the following general structure:

in which X is a halogen such as —F or —Cl; R is —H, —F, —Cl, —CF₃, or —CH₃; and the nitro group (—NO₂) is either meta or para with respect to R. A tris(nitrophenoxy)phenyl phosphine oxide compound is formed by this mixture. The method concludes with reducing the tris(nitrophenoxy)phenyl phosphine oxide compound by catalytic hydrogenation in the presence of 5% palladium on activated carbon in a hydrogen atmosphere to form the trifunctional crosslinker.

In one embodiment of the method in which W is P═O, the halogenated nitrobenzene is selected from the group consisting of 1-fluoro-4-nitro-benzene, 1-chloro-4-nitro-benzene, 1,2-difluoro-4-nitro-benzene, 1,2-dichloro-4-nitro-benzene, 1-fluoro-2-methyl-4-nitro-benzene, 1-chloro-2-methyl-4-nitro-benzene, 1-fluoro-2-(trifluoromethyl)-4-nitro-benzene, 1-chloro-2-(trifluoromethyl)-4-nitro-benzene, 1-methyl-2-chloro-4-nitrobenzene, 1-methyl-2-fluoro-4-nitro-benzene, 1-(trifluoromethyl)-2-chloro-4-nitro-benzene, 1-methyl-2-fluoro-4-nitro-benzene.

In another embodiment of the method in which W is P═O, the trifunctional crosslinker is selected from the group consisting of tris[(4-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-fluoro-5-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-fluoro-4-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-chloro-5-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-chloro-4-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-trifluoromethyl-5-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-trifluoromethyl-4-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-methyl-5-aminophenoxy)phenyl]phosphine oxide, and tris[4-(2-methyl-4-aminophenoxy)phenyl]phosphine oxide.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates an exemplary method for synthesizing triamine crosslinkers according to the present invention.

FIG. 2 illustrates the synthesis of an exemplary triamine crosslinker 1,1,1-tris[4-(4-aminophenoxyl)phenyl]ethane (TAPE, IV) having the general structure A (W is CH₃C).

FIG. 3 illustrates the synthesis of another exemplary triamine crosslinker tris[4-(4-aminophenoxyl)phenyl]phosphine oxide (TNPO, IX) having the general structure A (W is P═O).

FIGS. 4 and 5 illustrate exemplary halogenated nitrobenzene compounds and trifunctional crosslinkers according to the present invention.

DETAILED DESCRIPTION OF THE INVENTION

The present invention relates to multi-amine compounds that may be used to crosslink polyimides, polyamides, and poly(amide-imides) to create a covalent network structure that results in shape memory effects at elevated temperatures. The tetrahedral geometry and diphenylether linking groups of the presently disclosed tri- and tetrafunctional amine crosslinkers allow the synthesis of crosslinked polymers with both high-temperature tolerance and conformational flexibility. The present invention further includes methods of making the trifunctional amine crosslinkers.

The synthesis of a polyimide is typically accomplished by polymerization of a diamine and a dianhydride in a 1:1 molar ratio to generate a poly(amic acid) precursor, which is then converted to the corresponding polyimide typically by either thermal cure (heating to >200° C. in solution or solid state) or chemical imidization using a dehydrating agent or promoter such as acetic anhydride/triethylamine or acetic anhydride/pyridine. To generate a polyimide having the desired amount of crosslinking, an anhydride-terminated poly(amic acid) precursor is first generated by off-setting the dianhydride:diamine ratio so that the amount of dianhydride is in excess to cap both ends of the poly(amic acid) precursor. An appropriate amount of a multifunctional amine crosslinker is then be added to the precursor solution so that all the terminal anhydride groups will be consumed. Crosslinked polyimides may then be created using appropriate imidization conditions.

The synthesis of a polyamide is typically accomplished by two general methods. The first method involves polymerization of a diamine and a diacid chloride in a 1:1 molar ratio in an amide solvent such as N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMAc), N-methylpyrrolidone (NMP), etc. To generate a polyamide having the desired amount of crosslinking, an acid-chloride-terminated polymer is first generated by off-setting the diacid chloride:diamine ratio so that the amount of diacid chloride is in excess to cap both ends of the polymer. Subsequent addition of a multifunctional amine crosslinker in appropriate amounts to the acid-chloride-terminated polymer so that all the terminal acid chloride groups are consumed, immediately followed by casting and thermal curing under reduced pressure, leads to the crosslinked polyamide films.

The second method of synthesizing a polyamide involves polymerization of a diamine and a dicarboxylic acid with the aid of a promoter/catalyst combination such as triethylphosphite/pyridine (via Yamazaki-Higashi reaction) in an amide solvent such as N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMAc), N-methylpyrrolidone (NMP), etc. To generate a polyamide having the desired amount of crosslinking, a carboxylic acid-terminated polymer is first generated by off-setting the diacid:diamine ratio so that the amount of diacid monomer is in excess to cap both ends of the polymer. After the carboxylic acid-terminated polyamide has been isolated by precipitation in water and filtration, it is washed (water & methanol) and dried. It is then redissolved in an amide solvent and mixed with an amide solution of a multifunctional amine crosslinker in appropriate amounts so that all the terminal carboxylic-acid groups are consumed, which is immediately followed by casting and thermal curing under reduced pressure to create crosslinked polyamide films.

The synthesis of a poly(amide-imide) is typically accomplished by polymerization of a diamine and a trimellitic anhydride (TMA) or a dicarboxylic acid monomer derived from trimellitic anhydride aided by triethylphosphite/pyridine (Yamazaki-Higashi reagent) in a 1:1 molar ratio in an amide solvent such as N,N-dimethylformamide (DMF), N,N-dimethylacetamide (DMAc), N-methylpyrrolidone (NMP) etc. To generate a poly(amide-imide) having the desired amount of crosslinking, it is more suitable that a anhydride-terminated poly (amide-imide) is first generated via Yamazaki-Higashi reaction by off-setting TMA:diamine ratio so that the amount of TMA monomer is in excess to cap both ends of the polymer. After the anhydride-terminated polyamide has been isolated by precipitation in methanol and filtration, it is washed with methanol and dried in vacuo at 200° C. overnight. It is then redissolved in an amide solvent and mixed with an amide solution of a multifunctional amine crosslinker in appropriate amounts so that all the terminal carboxylic-acid groups are consumed, which is immediately followed by casting and thermal curing under reduced pressure to create crosslinked poly(amide-imide) films. Persons of skill in the art will appreciate that this polymerization method may be applied to other dianhydride monomers containing pre-formed aromatic amide moieties.

A triamine crosslinker according to the present invention exhibits the following general structure A, in which W is CH₃C (methylcarbyl), N (trivalent nitrogen), P═O (phosphine oxide), or BO₃ (borate; may also be written as B(—O)₃); R is —H, —F, —Cl, —CF₃, or —CH₃; and the amine groups (NH₂) may be in the meta or para position with respect to R:

In one embodiment, a tetraamine crosslinker according to the present invention exhibits the following general structures B or C, in which X is C or Si:

In another embodiment, a tetraamine crosslinker according to the present invention exhibits the following general structure D, in which Y is >C═O, —C(CF₃)₂—, —SO₂—, or —O—:

The present invention further includes methods of synthesizing triamine or trifunctional crosslinkers having the general structure A where W is CH₃C, N, or B(—O)₃, or P═O. FIG. 1 illustrates an exemplary method of making trifunctional crosslinkers according to the present invention starting from a tris(hydroxyphenyl) compound (I). Where W is CH₃C, N, B(—O)₃, or P═O, the tris(hydroxyphenyl) compound (I) may be 1,1,1-tris(4-hydroxyphenyl)ethane, tris(4-hydroxyphenyl)amine, tris(4-hydroxyphenyl)borate, or tris(4-hydroxyphenyl)phosphine oxide, respectively. A tris(nitrophenoxy)phenyl compound (III) is formed by mixing, in a polar, aprotic solvent, the tris(hydroxyphenyl) compound (I), a base such as potassium carbonate, and a halogenated nitrobenzene (II) having the following general structure:

On the halogenated nitrobenzene compound (II), X is a halogen such as —F or —Cl; R is —H, —F, —Cl, —CF₃, or —CH₃; and the nitro group (—NO₂) is either meta or para with respect to R. In one embodiment, the halogenated nitrobenzene (II) is selected from the group consisting of 1-fluoro-4-nitro-benzene, 1-chloro-4-nitro-benzene, 1,2-difluoro-4-nitro-benzene, 1,2-dichloro-4-nitro-benzene, 1-fluoro-2-methyl-4-nitro-benzene, 1-chloro-2-methyl-4-nitro-benzene, 1-fluoro-2-(trifluoromethyl)-4-nitro-benzene, 1-chloro-2-(trifluoromethyl)-4-nitro-benzene, 1-methyl-2-chloro-4-nitrobenzene, 1-methyl-2-fluoro-4-nitro-benzene, 1-(trifluoromethyl)-2-chloro-4-nitro-benzene, 1-methyl-2-fluoro-4-nitro-benzene. Suitable examples of a polar, aprotic solvent may include dimethylformamide (DMF), N,N-dimethylacetamide (DMAc), and N-methylpyrrolidone (NMP). The method concludes with reduction of the tris(nitrophenoxy)phenyl compound (III) by catalytic hydrogenation in the presence of 5% palladium on activated carbon in a hydrogen atmosphere to form the trifunctional crosslinker (IV).

FIGS. 4 and 5 illustrate several exemplary compounds according to the present invention. In FIG. 4, compounds X and XI are exemplary halogenated nitrobenzene compounds that may be used to synthesize trifunctional crosslinkers according to the present invention. X is 1-chloro-2-methyl-4-nitro-benzene, in which R (—CH₃) is meta to the nitro group, while XI is 1-(trifluoromethyl)-2-chloro-4-nitro-benzenes, in which R (—CF₃) is para to the nitro group. In FIGS. 4 and 5, compounds XII-XV are exemplary trifunctional crosslinkers according to the present invention. XII is 1,1,1-tris[4-(2-trifluoromethyl-5-aminophenoxy)phenyl]ethane, in which W is CH₃C and R (—CF₃) is para to the primary amine (—NH₂) XIII is tris[4-(2-chloro-4-aminophenoxy)phenyl]amine, in which W is N and R (—Cl) is meta to the primary amine. XIV is tris[4-(2-methyl-4-aminophenoxy)phenyl]borate, in which W is B(—O)₃ and R (—CH₃) is meta to the primary amine. XV is tris[4-(2-fluoro-5-aminophenoxy)phenyl]phosphine oxide, in which W is P═O and R (—F) is para to the primary amine.

In another embodiment of the method, W is CH₃C, and the trifunctional crosslinker is selected from the group consisting of 1,1,1-tris[4-(2-fluoro-5-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-fluoro-4-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-chloro-5-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-chloro-4-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-trifluoromethyl-5-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-trifluoromethyl-4-aminophenoxy)phenyl]ethane, 1,1,1-tris[4-(2-methyl-5-aminophenoxy)phenyl]ethane, and 1,1,1-tris[4-(2-methyl-4-aminophenoxy)phenyl]ethane.

In another embodiment, W is N, and the trifunctional crosslinker is selected from the group consisting of tris[4-(4-aminophenoxyl)phenyl]amine, tris[4-(2-fluoro-5-aminophenoxy)phenyl]amine, tris[4-(2-fluoro-4-aminophenoxy)phenyl]amine, tris[4-(2-chloro-5-aminophenoxy)phenyl]amine, tris[4-(2-chloro-4-aminophenoxy)phenyl]amine, tris[4-(2-trifluoromethyl-5-aminophenoxy)phenyl]amine, tris[4-(2-trifluoromethyl-4-aminophenoxy)phenyl]amine, tris[4-(2-methyl-5-aminophenoxy)phenyl]amine, and tris[4-(2-methyl-4-aminophenoxy)phenyl]amine.

In yet another embodiment, W is B(—O)₃, and the trifunctional crosslinker is selected from the group consisting of tris[4-(4-aminophenoxyl)phenyl]borate, tris[4-(2-fluoro-5-aminophenoxy)phenyl]borate, tris[4-(2-fluoro-4-aminophenoxy)phenyl]borate, tris[4-(2-chloro-5-aminophenoxy)phenyl]borate, tris[4-(2-chloro-4-aminophenoxy)phenyl]borate, tris[4-(2-trifluoromethyl-5-aminophenoxy)phenyl]borate, tris[4-(2-trifluoromethyl-4-aminophenoxy)phenyl]borate, tris[4-(2-methyl-5-aminophenoxy)phenyl]borate, and tris[4-(2-methyl-4-aminophenoxy)phenyl]borate.

In a further embodiment of the method, W is P═O, and the trifunctional crosslinker is selected from the group consisting of tris[4-(4-aminophenoxyl)phenyl]phosphine oxide, tris[4-(2-fluoro-5-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-fluoro-4-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-chloro-5-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-chloro-4-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-trifluoromethyl-5-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-trifluoromethyl-4-aminophenoxy)phenyl]phosphine oxide, tris[4-(2-methyl-5-aminophenoxy)phenyl]phosphine oxide, and tris[4-(2-methyl-4-aminophenoxy)phenyl]phosphine oxide.

As shown in FIG. 3 and discussed in more detail in the Examples, where W is P═O, the present invention further includes additional steps to synthesize the tris(hydroxyphenyl) compound (I in FIG. 1). Tris(4-methoxyphenyl)phosphine (V) is oxidized with aqueous hydrogen peroxide to form tris(4-methoxyphenyl)phosphine oxide (VI). The tris(4-methoxyphenyl)phosphine oxide (VI) is then demethylated by heating in pyridine hydrochloride to form the tris(hydroxyphenyl) compound (I in FIG. 1), in this case tris(4-hydroxyphenyl)phosphine oxide (VII in FIG. 3). As shown in FIGS. 1 and 3, the tris(hydroxyphenyl) compound (I) i.e. tris(4-hydroxyphenyl)phosphine oxide (VII) is mixed with a halogenated nitrobenzene (II in FIG. 1; not separately labeled in FIG. 3) and potassium carbonate in a polar, aprotic solvent to form a tris(nitrophenoxy)phenyl compound (III in FIG. 1) i.e. a tris(nitrophenoxy)phenyl phosphine oxide compound (VII in FIG. 3), which is then reduced by catalytic hydrogenation in the presence of 5% palladium on activated carbon in a hydrogen atmosphere to form the trifunctional crosslinker (IV in FIG. 1; IX in FIG. 3).

As discussed in more detail in the Examples, FIG. 2 illustrates the synthesis of one specific exemplary triamine crosslinker—1,1,1-tris[4-(4-aminophenoxyl)phenyl]ethane (TAPE, IV)—having the general structure A in which W is CH₃C and the halogenated nitrobenzene is 1-fluoro-4-nitro-benzene. FIG. 3 illustrates the synthesis of one specific exemplary triamine crosslinker—tris[4-(4-aminophenoxyl)phenyl]phosphine oxide (TNPO, IX)—having the general structure A in which W is P═O and the halogenated nitrobenzene is 1-fluoro-4-nitro-benzene.

The following examples and methods are presented as illustrative of the present invention or methods of carrying out the invention, and are not restrictive or limiting of the scope of the invention in any manner. Referring to the drawings, like reference numerals may designate like or corresponding parts throughout the several views.

Example 1

Synthesis of TNPE

The following is an exemplary procedure for the synthesis of one exemplary tris(nitrophenoxy)phenyl compound: 1,1,1-tris[4-(4-nitrophenoxyl)phenyl]ethane (TNPE, III) as depicted in FIG. 2. A tris(hydroxyphenyl) compound, which is 1,1,1-tris(4-hydroxyphenyl)ethane (THPE, I) (10.0 g, 33.0 mmol) in FIG. 2, a halogenated nitrobenzene, which is 1-fluoro-4-nitrobenzene (II) (15.4 g, 109 mmol) in FIG. 2, potassium carbonate (15.1 g, 109 mmol), and DMF (100 mL) were placed into a 250 mL three-necked flask equipped with a magnetic stir bar and nitrogen inlet and outlet. The mixture was stirred at room temperature for 24 hours and filtered. The filtrate was diluted with ethyl acetate (400 mL), and the organic layer was separated. The organic layer was washed with water three times. It was then dried over anhydrous magnesium sulfate and filtered. The filtrate was concentrated to 75 mL on a rotary evaporator and stored in a refrigerator for several days to afford 11.2 g (51%) of off-white crystals, m.p. 98-99° C. MS (m/e): 669 (M⁺). Anal. Calcd. for C₃₈H₂₇N₃O₉: C, 68.18%; H, 4.06%; N, 6.27%; O, 21.50%. Found: C, 67.69%; H, 4.26%; N, 6.21%; O, 21.22%. FT-IR (KBr, cm⁻¹): 3076, 2979, 1586, 1513, 1486, 1344, 1248, 1165, 1107, 874, 846. ¹H-NMR (DMSO-d₆, δ in ppm): 2.26 (s, 3H, CH₃), 7.17-7.27 (m, 18H, Ar—H), 8.28-8.31 (d, 6H, Ar—H).

Example 2

Synthesis of TAPE

The following is an exemplary procedure for the synthesis of an exemplary triamine crosslinker 1,1,1-tris[4-(4-aminophenoxyl)phenyl]ethane (TAPE, IV) by reduction of TNPE (III) via catalytic hydrogenation as depicted in FIG. 2. TNPE (III) (5.0 g, 7.5 mmol), THF (50 mL), and 5% palladium on activated carbon (0.50 g) were added to a hydrogenation bottle. The bottle was secured on a Parr hydrogenation apparatus, flushed three times with hydrogen, and then pressurized to 55 psi. After the mixture had been agitated at room temperature for 24 hours under the hydrogen pressure of 55 psi, it was filtered through Celite. The filter cake was washed with THF, and then the filtrate was evaporated to dryness on a rotary evaporator to afford a 4.25 g (98%) of yellow crystal, which was used without further purification, m.p. 220-221° C. MS (m/e): 579 (M⁺). Anal. Calcd. for C₃₈H₃₃N₃O₃: C, 78.73%; H, 5.74%; N, 7.25%. Found: C, 78.17%; H, 5.78%; N, 7.04%. FT-IR (KBr, cm⁻¹): 3441, 3361 (NH₂), 3035, 2970, 1617, 1581, 1497, 1384, 1232, 1173, 1117, 1010, 871, 842. ¹H-NMR (DMSO-d₆, δ in ppm): 2.02 (s, 3H, CH₃), 4.99 (s, 6H, NH₂), 6.53-6.58 (d, 6H, Ar—H), 6.68-6.74 (m, 12H, Ar—H), 6.88-6.93 (d, 6H, Ar—H).

Example 3

Synthesis of TMPO

The following is an exemplary procedure for the synthesis of tris(4-methoxyphenyl)phosphine oxide (TMPO, VI) as depicted in FIG. 3. Into a 100 mL three-necked flask equipped with a magnetic stir bar and nitrogen inlet and outlet were placed tris(4-methoxyphenyl)phosphine (TMP, V) (3.0 g, 8.5 mmol) and acetone (30 mL). A mixture of water (2 mL) and H₂O₂ (35%, 1 mL, 9 mmol) was added slowly. After the mixture had been stirred at room temperature for 1 hour, the acetone was evaporated, and methylene chloride (50 mL) was added. The organic phase was washed with a saturated NaCl solution (35 mL) three times with the aid of a separatory funnel. The organic layer was then dried over anhydrous sodium sulfate. Finally, the solvent was removed via rotary evaporation to afford 3.0 g (95%) of a white solid, m.p. 144.7-145.4° C. MS (m/e): 368 (M⁺). Anal. Calcd. for C₂₁H₂₁O₄P: C, 68.47%; H, 5.75%; P, 8.41%. Found: C, 68.42%; H, 5.72%; P, 8.11%. FT-IR (KBr, cm⁻¹): 3068, 3026, 2959, 2837, 1597, 1569, 1503, 1468, 1289, 1254, 1179, 1121, 1019, 803, 671, 543. ¹H-NMR (CDCl₃, 6 in ppm): 3.84 (s, 6H, CH₃), 6.94-6.97 (dd, 6H, Ar—H), 7.54-7.60 (dd, 6H, Ar—H). ¹³C-NMR (DMSO-d₆, δ in ppm): 55.29, 114.08, 114.21, 124.19, 125.28, 133.21, 133.32, 161.79, 161.82.

Example 4

Synthesis of THPO

The following is an exemplary procedure for the synthesis of tris(4-hydroxyphenyl)phosphine oxide (THPO, VII) via demethylation of TMPO (VI) as depicted in FIG. 3. Into a 500 mL three-necked flask equipped with a magnetic stir bar and nitrogen inlet and outlet were placed TMPO (VI) (25.0 g, 67.9 mmol) and an excess of pyridine hydrochloride (250 g) at 210° C. for 2 hours. The light brown solution was poured into water while it was still hot. The white precipitate was collected and recrystallized from ethyl acetate to afford 21.0 g (95%) of white crystals, m.p. 274.8-276.8° C. MS (m/e): 326 (M⁺). FT-IR (KBr, cm⁻¹): 3380, 1601, 1581, 1505, 1436, 1278, 1175, 1119, 1068, 831, 677, 537. ¹H-NMR (DMSO-d₆, δ in ppm): 6.86-6.89 (dd, 6H, Ar—H), 7.32-7.38 (dd, 6H, Ar—H), 10.14 (s, 3H, OH). ¹³C-NMR (DMSO-d₆, δ in ppm): 115.32, 115.45, 122.59, 123.69, 133.29, 133.40, 160.28, 160.30.

Example 5

Synthesis of TNPO

The following is an exemplary procedure for the synthesis of tris[4-(4-nitrophenoxyl)phenyl]phosphine oxide (TNPO, XIII) as depicted in FIG. 3. Into a 250 mL three-necked flask equipped with a magnetic stir bar and nitrogen inlet and outlet were placed THPO (VII) (7.52 g, 20.0 mmol), 1-fluoro-4-nitrobenzene (II) (9.32 g, 66.0 mmol), potassium carbonate (9.14 g, 66.0 mmol), and DMF (100 mL) at 100° C. for 48 hours. The mixture was allowed to cool to room temperature and filtered. The filtrate was poured into water, and the precipitate was extracted with ethyl acetate (300 mL) three times with the aid of a reparatory funnel. The combined organic extract was concentrated under vacuum, and 13.3 g (97%) of yellow crystals that were formed during the concentrating process was collected by filtration, m.p. 205.0-206.6° C. MS (m/e): 689 (M⁺). FT-IR (KBr, cm⁻¹): 3071, 1612, 1585, 1523, 1487, 1345, 1242, 1176, 1116, 879, 866, 831, 788, 696, 556. ¹H-NMR (DMSO-d₆, δ in ppm): 7.27-7.31 (d, 6H, Ar—H), 7.35-7.37 (d, 6H, Ar—H), 7.75-7.80 (m, 6H, Ar—H), 8.27-8.31 (d, 6H, Ar—H). ¹³C-NMR (DMSO-d₆, δ in ppm): 118.84, 119.82, 119.94, 126.22, 128.18, 129.23, 134.09, 134.20, 143.09, 157.93, 157.96, 161.29.

Example 6

Synthesis of TAPO

The following is a procedure for the synthesis of another exemplary triamine crosslinker tris[4-(4-aminophenoxyl)phenyl]phosphine oxide (TAPO, XIV) having the general structure A where W is P═O (IUPAC name 4,4′,4″-(4,4′,4″-phosphinetriyltris(benzene-4,1-diyl)tris(oxy))trianiline) by reduction of TNPO (XIII) via catalytic hydrogenation as depicted in FIG. 3. TNPO (VIII) (8.0 g, 11.6 mmol), DMF (120 mL), and 5% palladium on activated carbon (0.50 g) were added to a hydrogenation bottle. The bottle was secured on a Parr hydrogenation apparatus, flushed three times with hydrogen, and then pressurized to 60 psi. After the mixture had been agitated at room temperature for 24 hours under the hydrogen pressure of 60 psi, it was filtered through a cake of Celite. The filter cake was washed with DMF. The filtrate was then poured into water to precipitate a white solid that was subsequently recrystallized from ethanol/water to afford 6.41 g (98%) of white crystal, m.p. 211.1-211.5° C. MS (m/e): 559 (M⁺). Anal. Calcd. for C₃₆H₃₀N₃O₄P: C, 72.11%; H, 5.04%; N, 7.01%. Found: C, 72.01%; H, 4.97%; N, 6.91%. FT-IR (KBr, cm⁻¹): 3437, 3328, 3210, 3042, 1592, 1507, 1493, 1242, 1197, 1165, 1117, 871, 830, 671, 577. ¹H-NMR (DMSO-d₆, δ in ppm): 5.06 (s, 6H, NH₂), 6.59-6.62 (d, 6H, Ar—H), 6.79-6.81 (d, 6H, Ar—H), 6.94-6.96 (d, 6H, Ar—H), 7.48-7.53 (d, 6H, Ar—H). ¹³C-NMR (DMSO-d₆, δ in ppm): 114.85, 115.89, 116.01, 121.34, 125.06, 126.13, 133.40, 133.51, 144.11, 146.13, 162.89, 161.92.

Example 7

Synthesis of a Crosslinked Polyimide

The following exemplary procedure demonstrates the utility of the presently disclosed triamine crosslinkers for the synthesis of crosslinked polyimide films. An exemplary fluorinated polyimide, CP2 (LaRC™-CP2, NASA Langley Research Center), was prepared by adding 1,3-bis(3-aminophenoxy)benzene (1.081 g, 3.700 mmol) and DMAc (14 mL) to a 50 mL three-necked flask equipped with a magnetic stirrer and a nitrogen inlet and outlet and stirred under dry nitrogen at room temperature for 30 minutes. An excess of 2,2-bis(phthalic anhydride)-1,1,1,3,3,3-hexafluoroisopropane (1.777, 4.000 mmol) was then introduced to the resulting solution. The light yellow solution was agitated at room temperature for 24 hours to afford a solution of poly(amic acid) oligomers (PAA oligomers). TAPE (IV) (0.1159 g, 0.200 mmol, 5 mol %) synthesized according to FIG. 2 and Examples 1 and 2 was added to the solution of PAA oligomers in DMAc. After the TAPE had completely dissolved, the resulting PAA sol-gel precursor solution was poured into a glass petri dish, followed by vacuum evaporation of the DMAc at 50° C. and heat-treatment according to following schedule: 100° C./2 hours, 150° C./2 hours, 175° C./1 hour, 200° C./2 hours, 250° C./1 hour, and 300° C./1 hour to form films consisting of xE-CP2. The resulting crosslinked polyimide films were approximately 20-100 μm in thickness. As compared to the T_g of about 219° C. for neat polyimide (CP2, data not shown), the crosslinked CP2 films comprising 5 mol % TAPE demonstrated a higher T_g of about 239° C.

Although this invention has been described with respect to certain preferred embodiments, various other embodiments and various changes and modifications to the disclosed embodiment(s) will become apparent to those skilled in the art. All such other embodiments, changes, and modifications are intended to come within the spirit and scope of the appended claims.