Reactive sealing compositions for sealing hydrocarbon containing subterranean formations and methods
US20050009710A1
2005-01-13
10/884,373
2004-07-02
Abstract:
The present invention provides a sealing composition for sealing a portion of a subterranean formation to prevent a flow of a liquid hydrocarbon into or from the portion of the subterranean formation and associated methods of use. The sealing compositions are basically comprised of water, a hydraulic cement, an organophillic clay, a hydratable gelling agent, and a water soluble alkaline source in effective amounts.
Inventors:
- Sears T. DEALY 10 🇺🇸 Comanche, OK, United States
- James F. Heathman 12 🇺🇸 Katy, TX, United States
Interested in similar patents?
Get notified when new applications in this technology area are published.
Classification:
C09K8/46 » CPC further
Compositions for drilling of boreholes or wells; Compositions for treating boreholes or wells, e.g. for completion or for remedial operations; Compositions for cementing, e.g. for cementing casings into boreholes; Compositions for plugging, e.g. for killing wells containing inorganic binders, e.g. Portland cement
C09K8/467 » CPC further
Compositions for drilling of boreholes or wells; Compositions for treating boreholes or wells, e.g. for completion or for remedial operations; Compositions for cementing, e.g. for cementing casings into boreholes; Compositions for plugging, e.g. for killing wells containing inorganic binders, e.g. Portland cement containing additives for specific purposes
C04B2103/0035 » CPC further
Function or property of ingredients for mortars, concrete or artificial stone; Standardised cement types according to API Type G
C04B24/20 » CPC further
Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers; Sulfur-containing compounds Sulfonated aromatic compounds
C04B24/226 » CPC further
Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers; Sulfur-containing compounds; Sulfonated aromatic compounds; Condensation or polymerisation products thereof Sulfonated naphtalene-formaldehyde condensation products
C04B14/10 » CPC further
Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone; Granular materials, e.g. microballoons; Silica-rich materials; Silicates Clay
C04B22/10 » CPC further
Use of inorganic materials as active ingredients for mortars, concrete or artificial stone, e.g. accelerators, shrinkage compensating agents; Acids or salts thereof containing carbon in the anion
C04B24/38 » CPC further
Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers; Macromolecular compounds Polysaccharides or derivatives thereof
C04B22/002 » CPC further
Use of inorganic materials as active ingredients for mortars, concrete or artificial stone, e.g. accelerators, shrinkage compensating agents Water
C04B22/062 » CPC further
Use of inorganic materials as active ingredients for mortars, concrete or artificial stone, e.g. accelerators, shrinkage compensating agents; Oxides, Hydroxides of the alkali or alkaline-earth metals
C04B24/22 » CPC further
Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers; Sulfur-containing compounds; Sulfonated aromatic compounds Condensation or polymerisation products thereof
C04B24/383 » CPC further
Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers; Macromolecular compounds; Polysaccharides or derivatives thereof Cellulose or derivatives thereof
C04B28/02 » CPC main
Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
C04B14/104 » CPC further
Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone; Granular materials, e.g. microballoons; Silica-rich materials; Silicates; Clay Bentonite, e.g. montmorillonite
C04B14/28 » CPC further
Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone; Granular materials, e.g. microballoons; Carbonates of calcium
C04B22/0026 » CPC further
Use of inorganic materials as active ingredients for mortars, concrete or artificial stone, e.g. accelerators, shrinkage compensating agents; Water Salt water, e.g. seawater
C04B22/0093 » CPC further
Use of inorganic materials as active ingredients for mortars, concrete or artificial stone, e.g. accelerators, shrinkage compensating agents Aluminates
C04B2103/408 » CPC further
Function or property of ingredients for mortars, concrete or artificial stone; Surface-active agents, dispersants Dispersants
C04B2103/44 » CPC further
Function or property of ingredients for mortars, concrete or artificial stone Thickening, gelling or viscosity increasing agents
Description
CROSS-REFERENCE TO RELATED APPLICATIONThis application is a Continuation-in-part Application of commonly owned U.S. patent application Ser. No. 10/061,083, filed Jan. 31, 2002, entitled “Reactive Cement Compositions for Sealing Hydrocarbon Containing Subterranean Zones and Methods,” by James F. Heathman et al., which is hereby incorporated by reference herein for all purposes.
BACKGROUND OF THE INVENTIONThe present invention relates to improved reactive sealing compositions for sealing liquid hydrocarbon containing subterranean formations and methods of use.
In the drilling of oil and gas wells using the rotary drilling method, drilling fluid is circulated through the drill string and drill bit and then back to the surface by way of the wellbore being drilled. The drilling fluid maintains hydrostatic pressure on the subterranean formations through which the wellbore is drilled and circulates cuttings out of the wellbore. As the wellbore is drilled, formations are encountered which may be too weak to support the hydrostatic pressure of the drilling fluid column, or they have large natural fractures, vugs, or other passages which allow the drilling fluid to flow into the subterranean formations. Once the drilling fluid circulation is lost as a result of the drilling fluid entering a subterranean formation by way of fractures, vugs, or other passages, the drilling operations must be terminated while remedial steps are taken. Also, when a subterranean formation is penetrated containing fluids at a higher pressure than the hydrostatic pressure of the drilling fluid column, such fluids, e.g., liquid hydrocarbons, flow into the wellbore causing cross-flows or underground blowouts.
Hererofore, a variety of sealing compositions have been developed and used for combatting lost circulation, cross-flows, and underground blowouts. However, when the drilling fluid is a hydrocarbon-based fluid or when the fluid cross-flows or underground blowouts are liquid hydrocarbons, such sealing compositions have often been unsuccessful due to delayed and inadequate viscosity development by the sealing compositions.
Recently, oil-based and water-based compositions for sealing subterranean formations have been developed and utilized by Halliburton Energy Services, Inc., of Duncan, Okla. The compositions are the subject matter of U.S. Pat. No. 5,913,364 issued on Jun. 22, 1999 to Sweatman, U.S. Pat. No. 6,060,434 issued on May 9, 2000 to Sweatman et al. and U.S. Pat. No. 6,167,967 issued on Jan. 2, 2001 to Sweatman. While the compositions described in the above patents are very reactive, i.e., they very quickly develop viscosity and have been utilized successfully when the drilling fluid is an aqueous fluid or the cross-flow or blowout fluid is formation water, the sealing composition is not reactive when the fluid in the wellbore is a liquid hydrocarbon fluid.
More recently, very reactive water-based sealing compositions have been developed and utilized by Halliburton Energy Services, Inc., of Duncan, Okla., which are disclosed in U.S. Pat. No. 6,258,757 issued on Jul. 10, 2001 to Sweatman et al. While the sealing compositions are effective when the drilling fluid is a hydrocarbon-based fluid or the cross-flow or blowout fluid is a liquid hydrocarbon fluid and form relatively stiff unpumpable masses when placed and reacted, there are lost circulation, cross-flow, and blowout situations which require even greater resistance to flow and compressive strength in order to contain liquid hydrocarbon fluids.
Thus, there are continuing needs for improved lost circulation, cross-flow or blowout sealing compositions which are very reactive and form high strength masses which have compressive strengths when placed and reacted with liquid hydrocarbons.
SUMMARY OF THE INVENTIONThe present invention relates to improved reactive sealing compositions for sealing liquid hydrocarbon containing subterranean formations and associated methods of use.
In one embodiment, the present invention provides a sealing composition for sealing a portion of a subterranean formation to prevent a flow of a liquid hydrocarbon into or from the portion of the subterranean formation comprising a water, a hydraulic cement, an organophillic clay, a hydratable gelling agent, and a water soluble alkaline source.
In one embodiment, the present invention provides a sealing method of sealing a portion of a subterranean formation to prevent a flow of a liquid hydrocarbon into or from the portion of the subterranean formation comprising the steps of providing a subterranean formation sealing composition comprising water, a hydraulic cement, an organophillic clay, a hydratable gelling agent, and a water soluble alkaline source; and introducing the subterranean formation sealing composition into the subterranean formation.
In one embodiment, the present invention provides a sealing method of sealing a portion of a subterranean formation to prevent a flow of a liquid hydrocarbon into or from the portion of the subterranean formation comprising the steps of providing a subterranean formation sealing composition comprising water, a hydraulic cement, an organophillic clay, a hydratable gelling agent and a water soluble alkaline source; and introducing the subterranean formation sealing composition into the subterranean formation such that the sealing composition contacts the liquid hydrocarbons thereby forming a sealing mass.
The objects, features and advantages of the present invention will be readily apparent to those skilled in the art upon a reading of the description of preferred embodiments which follows.
DESCRIPTION OF PREFERRED EMBODIMENTSThe present invention relates to improved reactive sealing compositions for sealing liquid hydrocarbon containing subterranean formations and associated methods of use.
The sealing compositions of the present invention are basically comprised of water, a hydraulic cement, an organophillic clay, a hydratable gelling agent, and a water soluble alkaline source. The organophillic clay instantaneously reacts with liquid hydrocarbons in the wellbore to form a high viscosity, semi-rigid sealing mass. The gelation and/or hydration of the hydraulic cement by the water is accelerated by the alkaline source in the compositions to quickly provide flow resistance and compressive strength to the compositions. The hydratable gelling agent is present in the compositions to maintain the solids in suspension in the compositions.
The water, in addition to hydrating the hydraulic cement, is present in a quantity sufficient to produce a pumpable slurry. The water may be from any source provided it does not contain compounds that adversely affect the components in the sealing compositions. The water can be fresh water or salt water. The term “salt water” is used herein to mean unsaturated salt solutions and saturated salt solutions including brines and sea water. Generally, the water is present in the sealing composition of the present invention in an amount in the range of from about 15% to about 75% by weight of the compositions, more preferably in the range of from about 20% to about 45%.
A variety of hydraulic cements can be utilized in accordance with present invention including those comprised of calcium, aluminum, silicon, oxygen, and/or sulfur which set and harden by reaction with water. Such hydraulic cements include Portland cements, pozzolanic cements, gypsum cements, aluminous cements, silica cements, and slag cements. The cements can be of conventional particle sizes or they can be of ultra-fine particle sizes. Portland cements are generally preferred for use in accordance with the present invention. Portland cements of the types defined and described in API Specification For Materials And Testing For Well Cements, API Specification 10, 5th ed., dated Jul. 1, 1990, of the American Petroleum Institute are particularly suitable. Preferred such API Portland cements include classes A, B, C, G, and H. The hydraulic cement used is included in the sealing compositions of the present invention in an amount in the range of from about 5% to about 60% by weight of the composition, more preferably in an amount of from about 10% to about 40%.
While various organophillic clays can be utilized, an alkyl quaternary ammonium bentonite clay is preferred. A particularly suitable alkyl quaternary ammonium bentonite clay for use in accordance with the present invention is commercially available from Southern Products, Inc., of Gonzales, Tex., under the trade designation “CLAYTONE-II™.” The organophillic clay utilized is generally present in the composition of the present invention in an amount in the range of from about 20% to about 60% by weight of the composition, more preferably from about 30% to about 40%.
A variety of hydratable gelling agents can be utilized in accordance with the present invention. Preferred such hydratable gelling agents which yield high viscosities upon hydration include one or more of guar gum and guar derivatives such as hydroxypropylguar and carboxymethylguar, cellulose derivatives such as hydroxyethylcellulose, carboxymethylcellulose, and carboxymethylhydroxyethyl-cellulose, locust bean gum, carragenan gum, xanthan gum, and welan gum. Of these, welan gum is preferred. The hydratable gelling agent or agents used are included in the sealing composition of the present invention in an amount in the range of from about 0.1% to about 1% by weight of the composition, more preferably from about 0.1% to about 0.5%.
The viscosities of the gelling agents when hydrated in the sealing composition water can be increased by combining one or more crosslinking agents with the gelled solution. Examples of crosslinking agents which can be utilized are multivalent metal salts or compounds which are capable of releasing the metal ions in an aqueous solution. Examples of such multivalent metal ions are chromium, zirconium, antimony, titanium, iron (ferrous or ferric), zinc, or aluminum. When used, a crosslinking agent as described above is included in the sealing composition of the present invention in an amount in the range of from about 0.1% to about 3% by weight of the composition, more preferably from about 0. 1% to about 1%.
The water soluble alkaline is a known cause of gelation and excessive viscosity, and premature gelation when present in hydraulic cement slurries. In order to facilitate the rapid gelation and viscosification of the hydraulic cement component of the sealing composition of the present invention, a water soluble alkaline source, such as sodium hydroxide, sodium aluminate, or sodium carbonate, functions as a pH buffer and gelation and/or set accelerating agent for the hydraulic cement in the sealing composition and is generally present in the sealing composition in an amount in the range of from about 1% to about 15% by weight of the composition, more preferably from about 1% to about 10%.
In order to provide an acid solution removable water insoluble bridging agent in the sealing composition to bridge over permeable portions of the walls of formations being sealed, particulate calcium carbonate can be included in the sealing composition. When used, the particulate calcium carbonate is included in the composition in an amount in the range of from about 5% to about 40% by weight of the composition.
Optionally, light weight additives may be added to the sealing composition of the present invention, inter alia, to reduce the density of the sealing composition. Any light weight additives compatible with the subterranean sealing composition may be used, including, but not limited to microspheres. Examples of suitable microspheres include, but are not limited to cenospheres, glass hollow microspheres, and ceramic hollow microspheres. An example of a suitable microsphere is commercially available from Halliburton Energy Services, Inc., of Houston, Tex., under the tradename, “SPHERELITE.” Where included, the microspheres are present in the sealing composition in an amount sufficient to provide a sealing composition having a density in a desired range.
In order to facilitate the dispersal of particulate solid materials in the sealing composition, e.g., the hydraulic cement and the organophillic clay, a dispersing agent (surfactant) can be included in the composition. While a variety of dispersing agents can be utilized, preferred dispersing agents are the condensation reaction product of acetone, formaldehyde, and sodium sulfite, the condensation reaction product of sodium naphthalene sulfonate and formaldehyde, and sodium-N-methyl-N-oleyltaurine mixed with sulfate liquor. Of these, the condensation reaction product of acetone, formaldehyde, and sodium sulfite is most preferred. When used, the dispersing agent is included in the composition of the present invention in an amount in the range of from about 0.1% to about 5% by weight of the composition, more preferably from about 0.1% to about 3%.
A variety of other suitable additives may be added to the sealing composition to alter its physical properties. It will be understood that such additives may include slurry density modifying materials (e.g., silica flour, silica fume, sodium silicate, synthetic hollow microspheres, natural or fly ash-derived hollow microspheres, microfine sand, iron oxides (hematite), barium sulfate (barite) and manganese oxides), dispersing agents, set retarding agents, set accelerating agents, fluid loss control agents, strength retrogression control agents, fillers, defoamers, silicas, and viscosifying agents.
The sealing compositions of the present invention can also be foamed with nitrogen or other suitable gas in the presence of a foaming agent and foam stabilizer for reducing the densities of the compositions, preventing fluid loss, and aiding in the diversion of the compositions into the subterranean formations to be sealed.
An example of a sealing composition of the present invention for sealing a portion of a subterranean formation to prevent the flow of liquid hydrocarbons into or from the portion of a subterranean formation comprises a water present in an amount in the range of from about 20% to about 50% by weight of the composition; a hydraulic cement present in an amount in the range of from about 20% to about 45% by weight of the composition; an organophillic clay present in an amount in the range of from about 10% to about 40% by weight of the composition; a hydratable gelling agent present in an amount in the range of from about 0.1% to about 0.8% by weight of the composition; and a sodium carbonate present in an amount in the range of from about 1% to about 15% by weight of the composition.
A more preferred sealing composition of the present invention for sealing a portion of a subterranean formation to prevent the flow of liquid hydrocarbons into or from the portion of a subterranean formation comprises: water present from about 25% to about 45% by weight of the composition; Portland cement present in an amount in the range of from about 20% to about 45% by weight of the composition; an alkyl quaternary ammonium bentonite clay present in an amount in the range of from about 10% to about 35% by weight of the composition; welan gum present in an amount in the range of from about 0.1% to about 0.5% by weight of the composition; and sodium carbonate present in an amount in the range of from about 1% to about 7% by weight of the composition.
As previously mentioned, the above composition can include particulate calcium carbonate, a dispersing agent and other cement composition additives.
The methods of the present invention for sealing a portion of a subterranean formation to prevent the flow of liquid hydrocarbons into or from the portion of the subterranean formation are comprised of the steps of providing a subterranean formation sealing composition comprised of water, a hydraulic cement, an organophillic clay, a hydratable gelling agent, and a water soluble alkaline source, preferably sodium carbonate; and introducing the sealing composition into the subterranean formation.
In order to further illustrate the compositions and methods of the present invention, the following example is given.
EXAMPLEThree sealing compositions of this invention were prepared. The first consisted of fresh water, API Class G Portland cement, calcium carbonate bridging agent, and organophillic clay. The second and third compositions consisted of fresh water, API Class G Portland cement, calcium carbonate bridging agent, organophillic clay, welan gum, sodium carbonate, and a dispersing comprised of acetone, formaldehyde, and sodium sulfite.
Each of the sealing compositions were reacted with equal volume amounts of kerosene, and the reaction times required for the mixtures to form semi-rigid, moldable consistencies are determined. The amounts of the various components in percent by weight of the sealing composition and the results of the tests are given in the Table below.
| TABLE |
| Reaction Times of Sealing Compositions When Contacted With Kerosene* |
| Sealing | Bridging | Organo- | Welan | Sodium | Dispersing | |||
| Compo- | Water, | Cement, | Agent, | phillic | Gum, | Carbonate, | Agent, | Reaction |
| sition | % by | % by | % by | Clay, % | % by | % by | % by | Time at |
| No. | weight | weight | weight | by weight | weight | weight | weight | 130° F. |
| 1 | 45 | 26 | 13.9 | 15.1 | — | — | — | >20 | min. |
| 2 | 45 | 25.91 | 13.9 | 12.8 | 0.12 | 2.09 | 0.18 | 8 | min. |
| 3 | 44.2 | 21.0 | 10.5 | 18.8 | 0.17 | 3.07 | 2.35 | <15 | sec. |
*all weight percentages in this table are by weight of the sealing composition as a whole |
From the Table, it can be seen that the sealing compositions of the present invention react very rapidly upon contact with hydrocarbons to form semi-rigid moldable sealing masses.
Thus, the present invention is well adapted to carry out the objects and attain the benefits and advantages mentioned as well as those which are inherent therein. While numerous changes to the compositions and methods can be made by those skilled in the art, such changes are encompassed within the spirit of the present invention as defined by the appended claims.
Claims
1. A sealing composition for sealing a portion of a subterranean formation to prevent a flow of a liquid hydrocarbon into or from the portion of the subterranean formation comprising:
a water present in an amount in the range of from about 15% to about 60% by weight of the composition;
a hydraulic cement present in an amount in the range of from about 15% to about 75% by weight of the composition;
an organophillic clay present in an amount in the range of from about 5% to about 60% by weight of the composition;
a hydratable gelling agent present in an amount in the range of from about 0.1% to about 1% by weight of the composition; and
a water soluble alkaline source.
2. The composition of claim 1 wherein the water is selected from the group consisting of fresh water and salt water.
3. The composition of claim 1 wherein the hydraulic cement is selected from the group consisting of Portland cements, pozzolanic cements, gypsum cements, aluminous cements, silica cements, and slag cements.
4. The composition of claim 1 wherein the hydraulic cement is Portland cement.
5. The composition of claim 1 wherein the organophillic clay is an alkyl quaternary ammonium bentonite clay.
6. The composition of claim 1 wherein the hydratable gelling agent is selected from the group consisting of one or more of guar gum, hydroxypropylguar, carboxymethylguar, hydroxyethylcellulose, carboxymethylcellulose, carboxymethylhydroxyethylcellulose, locust bean gum, carragenan gum, xanthan gum, and welan gum.
7. The composition of claim 1 wherein the hydratable gelling agent is welan gum.
8. The composition of claim 1 wherein the water soluble alkaline source is selected from the group consisting of sodium hydroxide, sodium aluminate, and sodium carbonate and is present in an amount in the range of from about 1% to about 15% by weight of the composition.
9. The composition of claim 1 which further comprises a particulate calcium carbonate present in an amount in the range of from about 5% to about 40% by weight of the composition.
10. The composition of claim 1 which further comprises a dispersing agent present in an amount in the range of from about 0.1% to about 5% by weight of the composition.
11. The composition of claim 10 wherein the dispersing agent is the condensation reaction product of acetone, formaldehyde, and sodium sulfite, or the condensation reaction product of sodium naphthalene sulfonate and formaldehyde, and sodium-N-methyl-N-oleyltaurine mixed with sulfate liquor.
12. A sealing composition for sealing a portion of a subterranean formation to prevent a flow of a liquid hydrocarbon into or from the portion of the subterranean formation comprising:
a water present in an amount in the range of from about 25% to about 50% by weight of the composition;
a Portland cement present in an amount in the range of from about 20% to about 45% by weight of the composition;
an alkyl quaternary ammonium bentonite clay present in an amount in the range of from about 10% to about 40% by weight of the composition;
a welan gum present in an amount in the range of from about 0.1% to about 0.5% by weight of the composition; and
a sodium carbonate present in an amount in the range of from about 1% to about 10% by weight of the composition.
13. The composition of claim 12 wherein the water is selected from the group consisting of fresh water and salt water.
14. The composition of claim 12 which further comprises particulate calcium carbonate present in an amount in the range of from about 5% to about 40% by weight of the composition.
15. The composition of claim 12 which further comprises a dispersing agent present in an amount in the range of from about 0.1% to about 3% by weight of the composition.
16. The composition of claim 15 wherein the dispersing agent is the condensation product of acetone, formaldehyde and sodium sulfite, or the condensation reaction product of sodium naphthalene sulfonate and formaldehyde, and sodium-N-methyl-N-oleyltaurine mixed with sulfate liquor.
17. A sealing method of sealing a portion of a subterranean formation to prevent a flow of a liquid hydrocarbon into or from the portion of the subterranean formation comprising the steps of:
providing a subterranean formation sealing composition comprising water, a hydraulic cement, an organophillic clay, a hydratable gelling agent, and a water soluble alkaline source; and
introducing the subterranean formation sealing composition into the subterranean formation.
18. The method of claim 17 wherein the water is selected from the group consisting of fresh water and salt water and is present in an amount in the range of from about 15% to about 60% by weight of the composition.
19. The method of claim 17 wherein the hydraulic cement is Portland cement and is present in an amount in the range of from about 15% to about 75% by weight of the composition.
20. The method of claim 17 wherein the organophillic clay is an alkyl quaternary ammonium bentonite clay and is present in an amount in the range of from about 5% to about 40% by weight of the composition.
21. The method of claim 17 wherein the hydratable gelling agent is a welan gum and is present in an amount in the range of from about 0.1% to about 1% by weight of the composition.
22. The method of claim 17 wherein the water soluble alkaline source is selected from the group consisting of sodium hydroxide, sodium aluminate, and sodium carbonate and is present in an amount in the range of from about 1% to about 15% by weight of the composition.
23. The method of claim 17 wherein the sealing composition further comprises particulate calcium carbonate present in an amount in the range of from about 5% to about 40% by weight of the composition.
24. The method of claim 17 wherein the sealing composition further comprises a dispersing agent present in an amount in the range of from about 0.1% to about 3% by weight of the composition.
25. The method of claim 17 wherein the dispersing agent is the condensation reaction product of acetone, formaldehyde and sodium sulfite, and is present in an amount in the range of from about 0.1% to about 3% by weight of the composition.
26. A sealing method of sealing a portion of a subterranean formation to prevent a flow of a liquid hydrocarbon into or from the portion of the subterranean formation comprising the steps of:
providing a subterranean formation sealing composition comprising water, a hydraulic cement, an organophillic clay, a hydratable gelling agent and a water soluble alkaline source; and
introducing the subterranean formation sealing composition into the subterranean formation such that the sealing composition contacts the liquid hydrocarbon thereby forming a sealing mass.