Method for manufacturing high-efficiency protective paper having functions of heat dissipation, heat conduction and electromagnetic absorption

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a method for manufacturing a high-efficiency protective paper having functions of heat dissipation, heat conduction and electromagnetic absorption, which enables to increases efficiency of 3-dimensional heat dissipation and conduction and to significantly absorb electromagnetic radiation.

2. Description of Related Art

With the rapid development of technology, the volume of electronic components tends to be decreased, and the density and performance of electronic components per unit area become increased. As a result, a total heat generation of the electronic component is yearly increased, and a traditional heat dissipating device cannot afford to dissipate the total heat generation quickly. If the heat generated by the electronic component is not removed efficiently, it will leads to an electronic ionization and a thermal stress situation of the electronic component, which reduces an overall stability and a service life of the electronic component. Accordingly, it is imperative to dissipate the heat generated from the electronic component to prevent a overheat situation thereof In addition, constantly increasing the frequency and transmission speed of electronic components also results in serious situations of electromagnetic interference and electromagnetic wave spillover.

SUMMARY OF THE INVENTION

In view of the above-mentioned problems, the object of the present invention is to provide a method for manufacturing a high-efficiency protective paper having functions of heat dissipation, heat conduction and electromagnetic absorption, which enables to increase efficiency of 3-dimensional heat dissipation and conduction and is to absorb electromagnetic radiation.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flow chart showing equipment used in the present invention;

FIG. 2 is a flow chart showing a method for manufacturing a high-efficiency protective paper having functions of heat dissipation, heat conduction and electromagnetic absorption according to the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

Hereinafter, an exemplary embodiment of the present invention will be described in detail with reference to the accompanying drawings.

As showed in FIG. 1 and FIG. 2, a flow chart showing equipment used in the present invention and a flow chart showing a method for manufacturing a high-efficiency protective paper having functions of heat dissipation, heat conduction and electromagnetic absorption according to the present invention are disclosed. The method comprises the following steps of:

(a) transferring a substrate by a feeding mechanism (1), wherein the substrate is a fiber mesh fabric, a non-woven fabric, a carbon fiber fabric or a carbon fiber non-woven fabric;

(b) evenly distributing a thermal conductive composite in a feed tank (2) over the substrate to form a hybrid material, wherein the thermal conductive composite is made by is made by fully mixing one or more of graphene oxide, expanded graphite and oxidized carbon nanotube with a metal salt and a nano-scale magnetic metal oxide, and wherein the metal salt is one or more of iron, cobalt, nickel, organic iron, organic nickel, organic cobalt, ferrocene, nickelocene and cobaltocene;

(c) leveling the hybrid material by a leveling mechanism (3) to flat a surface of the hybrid material;

(d) synchronously driving a roller for rolling the hybrid material by a rolling mechanism (4) to form a protective paper having a dense structure; preferably, the step (d) is repeated several times to achieve the dense structure;

(e) rolling up the protective paper by a receiving mechanism (5); and

(f) cutting the protective paper into a size as needed to be further placed inside a vacuum furnace, evacuating the vacuum furnace to have a negative pressure of at least 0.001 Pa, heating the vacuum furnace to a temperature of at least 400° C. at a heating rate of 50° C. per minute, maintaining the temperature of at least 400° C. for at least 4 hours in the vacuum furnace, and naturally cooling the protective paper down to a temperature of 100° C. As a result, the preparation of the protective paper is completed, and the prepared protective paper is taken out from the vacuum furnace.

The protective paper has the metal salt, e.g. one or more of iron, cobalt, nickel, organic iron, organic nickel, organic cobalt, ferrocene, nickelocene, cobaltocene and the like, which can be decomposed into pure iron, cobalt or nickel at a high temperature to act as a catalyst for the graphene oxide, expanded graphite or oxidized carbon nanotube. Additionally, in a carbon source environment, the protective paper can form long graphene or carbon nanotube by a higher temperature of at least 400° C., so that the protective paper has a higher and long-lasting elasticity, which can rebound at least 50%. Accordingly, the protective paper can be reused and has high efficiency of 3-dimensional heat dissipation and conduction as well as efficient absorption of electromagnetic radiation.

Compared with the technique available now, the present invention has the advantages of improving efficiency of 3-dimensional heat dissipation and conduction of the electronic components and significantly absorbing electromagnetic radiation, so the present invention has increased practicality for the overall implementation