ELECTRICALLY CONDUCTIVE FOAM

Description

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional application of U.S. patent application, entitled “ELECTRICALLY CONDUCTIVE FOAM AND APPLICATION METHOD FOR SAME”, with application Ser. No. 12/541,134, filed on Aug. 13, 2009, which claims foreign priority based on Chinese Patent application No. 200910302259.0, filed in China on May 13, 2009. The contents of the above-referenced applications are hereby incorporated by reference.

BACKGROUND

1. Technical Field

The present disclosure relates to foam, and particularly to electrically conductive foam and a method of applying the electrically conductive foam.

2. Description of Related Art

Generally, an electrically conductive gasket may be shielded from electro-magnetic interference (EMI) by covering the conductive gasket with foam and a layer of electrically conductive cloth. The conductive cloth may be made of highly conductive and anti-corrosive fabric, where an electrically conductive adhesive tape is usually provided on the conductive cloth. In use, the electrically conductive gasket should be manually cut into a required shape, and affixed to a surface of an electronic component using the conductive adhesive tape.

However, it is time-consuming to cut the electrically conductive gasket especially when there are many electrically conductive gaskets needed to be cut. The electrically conductive gasket also may not be properly contacted with a surface of the electronic component because of carelessness of an operator, which results in the reduction or lose of EMI shielding performance of the electrically conductive gasket.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flowchart of an exemplary embodiment of a method of applying electrically conductive foam.

FIG. 2 is an exploded, isometric view of an exemplary embodiment of a sprayer for spraying the electrically conductive foam.

DETAILED DESCRIPTION

An exemplary embodiment of electrically conductive foam includes electrically conductive material, plastic material, propellant, surfactant, and auxiliary material.

The electrically conductive material includes graphite grains or metal grains having good electrically conductive performance. In one embodiment, the electrically conductive material accounts for about 5% to about 10% of the electrically conductive foam by weight.

The plastic material includes polyisobutyl methacrylate or acrylic resin. In one embodiment, the plastic material accounts for about 10% to about 16% of the electrically conductive foam by weight.

The propellant is a liquid such as ethylene-vinyl acetate copolymer, polyethylene, or butane having high-pressure, and has high solubility and volatility performance. The propellant is capable of dissolving and frothing the electrically conductive material and plastic material to make the electrically conductive material become into foam. In one embodiment, the propellant accounts for about 65% to about 75% of the conductive foam by weight.

In one embodiment, the surfactant is sorbitan trioleate, and is used to control viscosity of the electrically conductive material dissolved by the propellant, and also to enhance the frothing of the propellant. In one embodiment, the surfactant accounts for about 0.5% to about 4% of the electrically conductive foam by weight.

The auxiliary material may include at least one of plasticizer, silicon rubber, pigment, and flame retardant. The plasticizer can be used to reduce the viscosity of the electrically conductive material frothed by the propellant. The silicon rubber makes the electrically conductive foam easily removable from an electronic component. The pigment can be used to modify color of the electrically conductive foam. The flame retardant can be used to make the electrically conductive foam flame retardant. In one embodiment, the auxiliary material accounts for about 4% to about 5% of the electrically conductive foam by weight.

The weight proportions of the electrically conductive material, the plastic material, and the propellant can be modified as needed to suit specific needs. For example, when the electrically conductive foam needs to have a higher electrically conductive performance, more electrically conductive material can be added to the electrically conductive foam.

Referring to FIG. 1 and FIG. 2, a method of applying the conductive foam is provided, which includes the following steps.

In step S1, the electrically conductive foam and liquid pressurized gas such as nitrogen or dimethyl are put into a sprayer 1. The liquid pressurized gas makes pressure inside the sprayer 1 to be much higher than outside the sprayer 1. The sprayer 1 includes a jar body 110, a sucker 120, a jar lid 150, a nozzle 130, and a spray pipe 140. The spray pipe 140 may be formed with different shapes to make the conductive foam eject with a required shape. Therefore, a plurality of spray pipes 140 with different shapes may be provided for a variety of needs. The jar body 110 includes an airproof cover 111. The nozzle 130 includes a pressing device 131, an opening 132, and a spout 133. A first end 121 of the sucker 120 extends into the inside of the jar body 110. A second end 122 opposite to the first end 121 of the sucker 120 passes through the airproof cover 111 of the jar body 110 and extends to the outside of the jar body 110.

In step S2, the sprayer 1 is shaken to mix the components of the electrically conductive foam and the liquid pressurized gas.

In step S3, the pressing device 131 is pressed to communicate the opening 132 with the spout 133 via well known technology. According to Bernoulli's principle, because the pressure inside the sprayer 1 is much higher than the external pressure, the conductive foam rises along the sucker 120 and is ejected, and may be directed to a surface of the electronic component, to provide electro-magnetic interference (EMI) shielding, via the spout 133 and the spray pipe 140. Once ejected, the electrically conductive foam solidifies as the liquid pressurized gas volatilizes, and the plastic material expands quickly.

One side of the jar lid 150 defines a handle 151. One end of the spray pipe 140 forms a pothook 141 corresponding to the handle 151. The spray pipe 140 can be hung on the side of the jar lid 150 via the pothook 141 engaging the handle 151 for storage purposes.

The conductive foam mentioned above does not need to be cut into a required shape, and can be properly contacted with the surface of the electronic component in a consistent manner to prevent EMI.

It is to be understood, however, that even though numerous characteristics and advantages of the present disclosure have been set forth in the foregoing description, together with details of the structure and function of the disclosure, the disclosure is illustrative only, and changes may be made in details, especially in matters of shape, size, and arrangement of parts within the principles of the disclosure to the full extent indicated by the broad general meaning of the terms in which the appended claims are expressed.